The effect of reduction temperature on Co-Mo/Al2O3 catalysts for carbon nanotubes formation

Siang Piao Chai; Sharif Hussein Sharif Zein; Abdul Rahman Mohamed

doi:10.1016/j.apcata.2007.04.020

The effect of reduction temperature on Co-Mo/Al₂O₃ catalysts for carbon nanotubes formation

Siang Piao Chai, Sharif Hussein Sharif Zein, Abdul Rahman Mohamed

Résultat de recherche: Article › examen par les pairs

69 Citations (Scopus)

Résumé

Catalyst reduction temperature was observed to affect the yield and diameter uniformity of carbon nanotubes (CNTs) produced on Co-Mo/Al₂O₃ catalysts. The results show that on the whole, the reduced catalysts gave higher carbon yield. The CNTs obtained from the unreduced catalyst and the catalysts reduced at 400, 550, and 700 °C had diameters of 9.0 ± 1.4, 11.0 ± 1.8, 11.2 ± 1.8, and 12.1 ± 2.7 nm, respectively, showing that an increase in catalyst reduction temperature produced a slightly larger average diameter and wider diameter distribution. Raman spectra further elucidate that better-graphitized CNTs were produced on the catalysts reduced with increasing reduction temperatures.

Langue d'origine	English
Pages (de-à)	173-179
Nombre de pages	7
Journal	Applied Catalysis A: General
Volume	326
Numéro de publication	2
DOI	https://doi.org/10.1016/j.apcata.2007.04.020
Statut de publication	Published - juill. 15 2007
Publié à l'externe	Oui

Note bibliographique

Funding Information:
The authors gratefully acknowledge the financial support provided by the Academy of Sciences Malaysia under Scientific Advancement Grant Allocation (SAGA) (project: A/C No. 6053001).

ASJC Scopus Subject Areas

Catalysis
Process Chemistry and Technology

Accès au document

10.1016/j.apcata.2007.04.020

Autres fichiers et liens

Citer

@article{e6a9287086ad4ab4a9a931fcc51ae4b7,

title = "The effect of reduction temperature on Co-Mo/Al2O3 catalysts for carbon nanotubes formation",

abstract = "Catalyst reduction temperature was observed to affect the yield and diameter uniformity of carbon nanotubes (CNTs) produced on Co-Mo/Al2O3 catalysts. The results show that on the whole, the reduced catalysts gave higher carbon yield. The CNTs obtained from the unreduced catalyst and the catalysts reduced at 400, 550, and 700 °C had diameters of 9.0 ± 1.4, 11.0 ± 1.8, 11.2 ± 1.8, and 12.1 ± 2.7 nm, respectively, showing that an increase in catalyst reduction temperature produced a slightly larger average diameter and wider diameter distribution. Raman spectra further elucidate that better-graphitized CNTs were produced on the catalysts reduced with increasing reduction temperatures.",

author = "Chai, {Siang Piao} and Zein, {Sharif Hussein Sharif} and Mohamed, {Abdul Rahman}",

note = "Funding Information: The authors gratefully acknowledge the financial support provided by the Academy of Sciences Malaysia under Scientific Advancement Grant Allocation (SAGA) (project: A/C No. 6053001).",

year = "2007",

month = jul,

day = "15",

doi = "10.1016/j.apcata.2007.04.020",

language = "English",

volume = "326",

pages = "173--179",

journal = "Applied Catalysis A: General",

issn = "0926-860X",

publisher = "Elsevier",

number = "2",

}

TY - JOUR

T1 - The effect of reduction temperature on Co-Mo/Al2O3 catalysts for carbon nanotubes formation

AU - Chai, Siang Piao

AU - Zein, Sharif Hussein Sharif

AU - Mohamed, Abdul Rahman

N1 - Funding Information: The authors gratefully acknowledge the financial support provided by the Academy of Sciences Malaysia under Scientific Advancement Grant Allocation (SAGA) (project: A/C No. 6053001).

PY - 2007/7/15

Y1 - 2007/7/15

N2 - Catalyst reduction temperature was observed to affect the yield and diameter uniformity of carbon nanotubes (CNTs) produced on Co-Mo/Al2O3 catalysts. The results show that on the whole, the reduced catalysts gave higher carbon yield. The CNTs obtained from the unreduced catalyst and the catalysts reduced at 400, 550, and 700 °C had diameters of 9.0 ± 1.4, 11.0 ± 1.8, 11.2 ± 1.8, and 12.1 ± 2.7 nm, respectively, showing that an increase in catalyst reduction temperature produced a slightly larger average diameter and wider diameter distribution. Raman spectra further elucidate that better-graphitized CNTs were produced on the catalysts reduced with increasing reduction temperatures.

AB - Catalyst reduction temperature was observed to affect the yield and diameter uniformity of carbon nanotubes (CNTs) produced on Co-Mo/Al2O3 catalysts. The results show that on the whole, the reduced catalysts gave higher carbon yield. The CNTs obtained from the unreduced catalyst and the catalysts reduced at 400, 550, and 700 °C had diameters of 9.0 ± 1.4, 11.0 ± 1.8, 11.2 ± 1.8, and 12.1 ± 2.7 nm, respectively, showing that an increase in catalyst reduction temperature produced a slightly larger average diameter and wider diameter distribution. Raman spectra further elucidate that better-graphitized CNTs were produced on the catalysts reduced with increasing reduction temperatures.

UR - http://www.scopus.com/inward/record.url?scp=34250378788&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34250378788&partnerID=8YFLogxK

U2 - 10.1016/j.apcata.2007.04.020

DO - 10.1016/j.apcata.2007.04.020

M3 - Article

AN - SCOPUS:34250378788

SN - 0926-860X

VL - 326

SP - 173

EP - 179

JO - Applied Catalysis A: General

JF - Applied Catalysis A: General

IS - 2

ER -